Pengaruh Proses Heat Treatment (Quenching dan Tempering) Terhadap Kekerasan dan Struktur Mikro Baja Karbon Menengah
Main Article Content
Abstract
Technological advances mean that steel production continues to be developed with better raw materials. Carbon steel is the one of the metals that is widely used in producing machining equipment, but it requires adjustment to the hardness and ductility properties of the steel must be heat treated to obtain properties according to its use from soft to hard. This research aims to determine the effect of cooling media in the quenching process and tempering process on hardness, tensile strength and microstructure. The variations used are variations in temperature and variations in water and oil quenching cooling media. The research method used was the experimental method, using descriptive statistical data analysis techniques, then hardness testing was carried out using the microvickers method, tensile testing, and microstructure observation. The research result showed that the highest hardness value was at a temperature variation of 900°C for the water-cooling medium with a hardness value of 490,1 VHN. The highest average tensile strength was produced by specimens with a heating temperature of 900°C with water cooling media, namely 1051,2 N/mm2. And the result of the microstructure test shows structural changes, namely the formation of a martensite structure due to the process of heating the austenite and the cooling it quickly.
Article Details
This work is licensed under a Creative Commons Attribution 4.0 International License.
References
Achmad Kusairi Samlawi Anton Tri Wibowo, "Pengaruh Proses Quenching Dengan Media Pendingin Air dan Oli Terhadap Kekerasan Baja dan Struktur Mikro Baja S45C", Jurnal Rotary Universitas Lambung Mangkurat, 2020.
Hartono Yudo, Sardjito Jokosisworo Muhammad Jordi, "Analisa Pengaruh Proses Quenching Dengan Media Berbeda Terhadap Kekuatan Tarik dan Kekerasan Baja St 36 Dengan Pengelasan SMAW", Jurnal Teknik Perkapalan Universitas Diponogoro, 2017.
Haryadi, Abdurrofi Zahrawani, Bintang Adjiantoro Iman Saefuloh, "Pengaruh Proses Quenching Dan Tempering Terhadap Sifat Mekanik Dan Struktur Mikro Baja Karbon Rendah Dengan Paduan Laterit", Jurnal Teknik Mesin Untirta, 2018.
Islami, Ratu Cludia Suwandi, et al. "Aplikasi Material Teknik Jenis Non Logam Diberbagai Industri Manufaktur Indonesia Secara Sistematik: Kajian Literatur." Prosiding Sains dan Teknologi 2.1 (2023): 343-351.
Agus Pramono, "Karakterisrik Mekanik Proses Hardening Baja Aisi 1045 Media Quenching Untuk Aplikasi Sprochet Rantai", Jurnal Teknik Metalurgi Universitas Sultan Ageng Tirtayasa, 2011.
Yopi Handoyo, "Pengaruh Quenching dan Tempering Pada Baja JIS Grade S45C Terhadap Sifat Mekanis dan Struktur Mikro Crankshaft", Universitas Islam 45 Bekasi, 2015.
Tjahjanti, P. H. (2019). Buku Ajar Pengetahuan Bahan Teknik. Umsida Press, 1-119.
Ali Achmadi, "Pengaruh Perlakuan Quenching Dengan Variasi Pendingin Konsentrasi Air Garam Terhadap Kekerasan dan Kekuatan Tarik Pada Baja ST 37", Jurnal Teknik Mesin STTR Cepu, 2017.
Sunyoto, Aryo Aji Prabowo, "Pengaruh Media Pendingin Pada Proses Quenching Terhadap Kekerasan, Struktur Mikro, dan Kekuatan Bending Baja AISI 1010", Jurnal Teknik Mesin Universitas Negeri Semarang, 2020.
Gunawan Dwi Haryadi, "Pengaruh Suhu Tempering Terhadap Kekerasan Struktur Mikro dan Kekuatan Tarik Pada Baja K-460", Jurnal Universitas Diponegoro, 2005.
Jufriadi, Ariefin, Edi Saputra, Mohd. Ghiffari, Hamdani, "Pengaruh Pengelasan dan Media Quenching Terhadap Kekuatan Tarik dan Kekerasan Material ASTM A36", Jurnal Politeknik Negeri Lhokseunawe, 2021.
Nugroho, Sri dan Gunawan, D H., "Pengaruh Media quenching Air tersirkulasi (Circilated Water) terhadap Struktur Mikro dan Kekerasan pada Baja AISI 1045". Surakarta: jurnal FKIP UNS, 2005.
Pramono, Agus, "Karakteristik Mekanik Proses Hardening Baja Aisi 1045 Media Quenching Untuk Aplikasi Sprochet Rantai", Banten: Jurnal Ilmiah Teknik Mesin Cakra, 2011.
Sarjono, K., "Pengaruh Hardening Pada Baja Jis G 4051 Grade S45c Terhadap Sifat Mekanis Dan Struktur Mikro", Jurnal Sains dan Teknologi Indonesia, 2012.
Septianto, B.A. and Setiyorini, Y., "Pengaruh Media Pendingin pada Heat Treatment Terhadap Struktur Mikro dan Sifat Mekanik Friction Wedge AISI 1340". Jurnal Teknik ITS, 2013.
Setiawan, Hera, "Pengaruh Proses Heat Treatment pada Kekerasan Material Special K (K100)", Kudus : Jurnal Teknik Mesin UMK, 2012.
Wattimena, dan Louhenapessy, j, "Pengaruh Holding Time dan Quenching terhadap Kekerasan Baja Karbon St 37 pada Proses Pack Carburizing menggunakan Arang Batok Pala", Jurnal Teknik Universitas Yogyakarta, 2014.
Trhutomo, prihanto, "Analisis Kekerasan Pada Pisau Berbahan Baja Karbon Menengah Hasil Proses Hardening Dengan Media Pendingin yang Berbeda", Jurnal Teknik Mesin ITS, 2015.